Polyvinyl chloride resin SG-7
Ngosipụta thermo plasticity, ịbụ onye a na-apụghị imeri emeri n'ime mmiri, mmanụ ụgbọala na mmanya na-aba n'anya, zara ma ọ bụ gbazee n'ime ether, ketone, chlorinated aliphatic hydrocarbons, na aromatic hydrocarbon, nnukwu iguzogide corrosion, na ezigbo ihe dielectric.
Nkọwapụta
Ụdị | SG3 | SG4 | SG5 | SG6 | SG7 | SG8 |
K uru | 72-71 | 70-69 | 68-66 | 65-63 | 62-60 | 59-55 |
Viscosity, ml/g | 135-127 | 126-119 | 118-107 | 106-96 | 95-87 | 86-73 |
Nkezi polymerization | 1350-1250 | 1250-1150 | 1100-1000 | 950-850 | 950-850 | 750-650 |
Ọnụọgụ nke oke adịghị ọcha | 30 | 30 | 30 | 30 | 40 | 40 |
Ọdịnaya na-ada ada % max | 0.4 | 0.4 | 0.4 | 0.4 | 0.4 | 0.4 |
Njupụta g/ml min | 0.42 | 0.42 | 0.42 | 0.45 | 0.45 | 0.45 |
Mwepụta mgbe sieve 0.25mm ntupu max | 2 | 2 | 2 | 2 | 2 | 2 |
0.063mm min | 90 | 90 | 90 | 90 | 90 | 90 |
Ọnụọgụ nke ọka/10000px2 max | 40 | 40 | 40 | 40 | 40 | 40 |
Plasticizer absorbency uru nke 100g resin | 25 | 22 | 19 | 16 | 14 | 14 |
Ọcha % min | 74 | 74 | 74 | 74 | 70 | 70 |
Mfọdu chlorethylene ọdịnaya mg/kg max | 5 | 5 | 5 | 5 | 5 | 5 |
Ethylidene chloride mg/kg max | 150 | 150 | 150 | 150 | 150 | 150 |
Ngwa
A na-eji SG-1 na-emepụta ihe mkpuchi ọkụ eletrik dị elu
A na-eji SG-2 na-emepụta ihe mkpuchi ọkụ, ngwaahịa dị nro na ihe nkiri
* A na-eji SG-3 na-emepụta ihe mkpuchi eletriki, ihe nkiri ugbo, ngwaahịa plastik a na-eji kwa ụbọchị,
dị ka ihe nkiri, mmiri ozuzo, mbukota ụlọ ọrụ, akpụkpọ anụ arụrụ arụ, eriri na akpụkpọ ụkwụ, wdg.
* SG-4 na-eji na-emepụta membranelle maka ulo oru na obodo ojiji, tube na ọkpọkọ
* SG-5 na-eji na-amị transperent ngwaahịa sectionbar, siri ike tube na ji achọ ihe, dị otú ahụ.
dị ka isiike efere, gramophone ndekọ, valueand ịgbado ọkụ mkpanaka, PVC ọkpọkọ, PVC windo, ọnụ ụzọ, wdg
* A na-eji SG-6 na-emepụta foil doro anya, bọọdụ siri ike na mkpanaka ịgbado ọkụ
* SG-7, SG-8 na-eji na-emepụta doro anya foil, hardinjection ịkpụzi.Good ike ike na elu ike, tumadi ji tubes na ọkpọkọ.